Abstract: In this study, the regeneration investigation for waste reverse osmosis membrane filters which were discarded after use for the household water purifiers has been carried out. Sodium hydroxide, sodium bisulfate, and ethylenediamine tetra acetic acid(EDTA). as the chemical cleaning agents were used. And they were in-situ cleaned with the micro-bubble generator as well. The best result was obtained when both 0.1% EDTA and micro-bubbles were used for 30 min cleaning. Thus, when the performance of the brand new RO membrane and restorated RO membrane were compared, the flux, 19.9%, the recovery ratio 45% were enhanced while the salt rejection was reduced for NaCl 100 mg/L solution, in other words, it has been recovered to the original brand new RO membrane filter. Also the removal of pollutants on membrane surface was confirmed in a naked eye through the scanning electron microscopy. Finally, this research has provided the possibility of the re-use of the waste RO membrane filters of household water purifier which were reclaimed or incinerated after use.

: 본 연구에서는 사용 후 폐기되는 정수기용 역삼투(Reverse Osmosis; RO)막 필터를 세정하여 새 필터의 수준으로 복원시키는 연구를 수행하였다. 화학적 세정액으로는 수산화나트륨, 중아황산나트륨, EDTA용액을 사용하였으며 마이크로버 블 발생 장치와 함께 in-situ의 방법으로 세정하였다. EDTA를 0.1%의 농도로 제조한 뒤 마이크로버블과 함께 사용하여 30분 세정하였을 때 가장 좋은 결과를 나타내었다. 이때 폐 필터와 세정 후 폐필터의 성능을 비교해 보았을 때 투과도는 19.9%, 회수율은 49.5%증가하였으며 NaCl 100 mg/L 용액에 대한 염제거율은 2.3% 감소되었는데, 이는 새 필터와 동등한 수준으로 회복이 되었다. 또한 전자현미경 분석을 이용하여 막 표면의 오염물의 제거를 육안으로 확인하였다. 이로써 전량 매립 또는 소각 되어지는 정수기용 폐 RO막 필터의 세정을 통하여 재사용이 가능할 것으로 판단된다.